IM9008

  • Call: (86)021-65054807 8008

My statusSkype send message to me Alibaba

  • Characteristic: medium toughness , biological source , biodegradable
    Used: PLA resin IM9005 is the toughened resin, suitable for products, such as toys, stationery, daily necessities, etc.
    Advantage: biological sources, biodegradable

  • 1. Description & Properties

    TJL PLA polymer IM9008 is a thermoplastic resin derived from annually renewable resources and is specifically designed for Injection Molding applications. The table below shows the properties of  IM9008.

    Appearance: White opaque pellets.

    Application：Injection Molding

    Odor: None.

     

    Item Unit Data Test Method
    Density g/cm3

    1.24

    ISO 1183
    Mass flow rate(210℃，2.16kG) g/10min

    5-10

    ISO 1133
    mould shrinkage %

    0.2-0.4

    ISO 294
    Tensile strength at break(10mm/min) MPa

    45

    ISO 527
    Elongation at break(10mm/min) %

    300

    ISO 527
    Flexural strength at break(2mm/min) MPa

    65

    ISO 178
    Flexural modulus(2mm/min) MPa

    2400

    ISO 178
    Notched impact strength(4mm，23℃) kJ/m2

    30

    ISO179/1eA
    Melting point(10℃/min) ℃

    160-170

    ISO11357
    Heat deflection temperature HDT/B(0.45MPa) ℃

    60

    ISO 75

     

    2. Applications & Propertie

    1. Toys：Toys for baby and pat

    2. Plastic products：packing box; stationery.

     

    3. Processing Information

    1. Drying 2. Injection Molding Temperature

    Drying Equipment

    desiccant dryer

    Rear – Zone 1 Temperature

    ℃

    ＜140

    Drying Temperature

    ℃

    80-90

    Middle – Zone 2 Temperature

    ℃

    170-190

    Drying Time

    h

    2-3

    Front – Zone 3 Temperature

    ℃

    180-210

    Moisture Content

    ppm

    ＜200

    Nozzle Temperature

    ℃

    190-220

    Hot Runner

    ℃

    180-210
    3.Others  

    Mold Temperature

    ℃

    100-120

    Screw Speed

    rpm

    50-150

    Injection Pressure

    MPa

    8-10